Bambu PLA Galaxy
PLA Galaxy -- where innovation meets elegance. Experience a new dimension of printing with filament infused with glass microsphere additives. This unique blend creates mesmerizing visual effects, offering dynamic reflections and a glossy, smooth finish. Elevate your prints to new heights as they gleam with unparalleled brilliance from every angle, all while maintaining the ease of printing and exceptional strength and toughness you expect from PLA Basic.
Appealing from Every Angle
PLA Galaxy's glass microsphere additives create unique light effects, offering dynamic reflections from various perspectives.
Sleek Glossy Finish
Enriched with glass microsphere additives, PLA Galaxy ensures a clear, seamlessly smooth surface texture, enhancing your prints with a captivating fluidity that is both dynamic and refined.
Effortless Printing
Crafted with premium materials, PLA Galaxy inherits the exceptional printability of PLA Basic, ensuring a hassle-free printing process.
| Recommended | Not Recommended | |
| Build Plate | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate | / |
| Hotend | Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm Hotend with Stainless Steel Nozzle 0.4 mm | Hotend with Stainless Steel Nozzle 0.2 mm |
| Glue | Bambu Liquid Glue / Glue Stick | / |
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 55 °C，8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 190 - 230 °C |
| Bed Temperature (with Glue) | 35 - 45 °C |
| Printing Speed | < 250 mm/s |
| Physical Properties | |
| Density | 1.19 g/cm³ |
| Vicat Softening Temperature | 56 °C |
| Heat Deflection Temperature | 52 °C |
| Melting Temperature | 156 °C |
| Melt Index | 11.0 ± 1.7 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 26 ± 3 MPa |
| Breaking Elongation Rate | 9.3 ± 1.1 % |
| Bending Modulus | 2200 ± 120 MPa |
| Bending Strength | 58 ± 3 MPa |
| Impact Strength | 55.4 ± 3.7 kJ/m² |
More Information
| Diameter | 1.75mm |
|---|